TLNPRO Smart

TLNPRO Smart- Two-component self-leveling pigmented epoxy compound without volatile solvents, for the installation of industrial polymer floor coverings

TLNPRO Smart -It is used indoors and outdoors as a base layer in TLNPRO industrial polymer floor coverings systems.

TLNPRO Smart -If necessary, it is allowed to use the material as a repair compound mixed with calcined quartz sand.

The ratio of binder/quartz sand and sand fractions must be selected based on the types of defects to be repaired.

TLNPRO Smart – has:

Resistance to high abrasion loads, including heavy vehicle traffic.
Good chemical resistance to fuels and lubricants, non-concentrated acids, salts and alkalis. Excellent spreading ability ensures a very smooth coating surface.
It does not contain volatile substances
It can be used as a repair compound.

TECHNICAL SPECIFICATIONS

The density of the mixture at a temperature of +23 ° C is 1.6 g/cm3
The viscosity of the mixture at a temperature of +23 ° C is 1,850 MPa · s
Processing time of the composition at a temperature of +23 ° C (30 kg set): 20-30 minutes
Material consumption 2.0 – 3.0 kg/m2
Polymerization time at +23°C:
pedestrian loads 24 hours
light transport loads 3 days
full transport load and chemical effects 7 days
Shore D hardness (after 7 days) 81
Appearance: Glossy surface
The interlayer interval:
+10°C at least after 15, maximum after 48
+23°C minimum after 8 hours, maximum after 48 hours
Storage: Store the material in the original packaging of the manufacturer in a dry, enclosed area, at a temperature of +5 to +30 ° C. Storage at a lower temperature can lead to crystallization of the components. Do not expose to direct sunlight.