TLNPRO Force

TLNPRO Force - Two-component epoxy primer with normal curing, free of volatile solvents, for dry and fresh concrete substrates with high humidity. It is used as a primer in systems of epoxy and polyurethane floor coverings.

TLNPRO Force - It is used as a dedusting impregnation of concrete and cement-sand foundations. It is allowed to use the material as a repair compound mixed with calcined quartz sand. The ratio of binder/quartz sand and sand fractions must be selected based on the types of defects to be repaired.

TLNPRO Force - Provides excellent adhesion of the polymer coating to the substrate. The material does not contain volatile organic substances, therefore, if necessary, it can be used as a universal repair compound. It has no unpleasant odor when applied.

TECHNICAL SPECIFICATIONS

The density of the mixture at a temperature of +20 ° C is 1.07 g/cm3
The viscosity of the mixture at a temperature of +23 ° C is 590 MPa · s
The processing time of the composition at 23 ° C (30 kg set) is 20-30 minutes
Material consumption 0.3 – 0.5 kg/m2
Polymerization time at +23 °C:
at +10°C 5 days
at +23°C 3 days
at +30°C 2 days
Compressive strength (after 28 days): 81 MPa
Tensile strength (after 7 days): 32 MPa
Shore D hardness (after 7 days) 83
Appearance Glossy surface
Storage: Store the material in the original packaging of the manufacturer in a dry, enclosed area, at a temperature of +5 to +30 ° C. Storage at a lower temperature can lead to crystallization of the components. Do not expose to direct sunlight.