TLNPRO Pure

ADD
TLNPRO Pure - Two-component economical pre-filled epoxy primer with normal curing, free of volatile solvents, for dry concrete substrates

  • It is used as a primer in TLNPRO epoxy floor coating systems.
  • It is allowed to use the material as a repair compound mixed with calcined quartz sand.
  • The ratio of binder/quartz sand and sand fractions must be selected based on the types of defects to be repaired.
  • As a highly filled mixture based on quartz sand for the manufacture of skirting boards with chips.
TLNPRO Pure:
  • Provides excellent adhesion of the polymer coating to the substrate.
  • The material does not contain volatile organic substances, therefore, if necessary, it can be used as a universal repair compound.
TECHNICAL SPECIFICATIONS

TECHNICAL SPECIFICATIONS

The density of the mixture at a temperature of +23 ° C is 1.44 g/cm3
The viscosity of the mixture at a temperature of +20 ° C is 1,400 MPa · s
Processing time of the composition at (set of 30 kg):
at +12 °C 60 minutes at +20 °C 30 minutes at +30°C 15 minutes
Material consumption 0.4 – 0.6 kg/m2
Polymerization time at +23 °C:
at +10°C 5 days
at +23°C 3 days
at +30°C 2 days
Shore D hardness (after 7 days) 79
Appearance: Glossy surface
Polymerization time:
at +10°C for 5 days
at +23°C for 3 days
at +30°C for 2 days
The interlayer interval:
at 10°C after a minimum of 16 hours, a maximum of 48 hours
at 23°C after a minimum of 6 hours, a maximum of 48 hours
at 30°C after a minimum of 3 hours, a maximum of 24 hours
Storage: Store the material in the original packaging of the manufacturer in a dry, enclosed area, at a temperature of +5 to +30 ° C. Storage at a lower temperature can lead to crystallization of the components. Do not expose to direct sunlight.